An Evaluation of Some Mechanical Properties of Autopolymerizing Acrylic Resin with the Modified One after Changing the Curing Environment: (In vitro Study)
Main Article Content
Abstract
Material and Methods: Standard acrylic specimens were fabricated according to ADA specification No.12 for transverse strength, ISO 179 was used for impact testing, Shore D for hardness and profilometerfor surface roughness. The material lignin first dispersed in the monomer, then the powder PMMA is immediately added. Ligninadded in different weight percentages. Then cured using pressure pot (Ivomet) in two temperatures;40°C and 80°C under 2 bar pressure, for 30 minutes.Atotal of 144samples were prepared for this study. Ts, Is, Ra, and Hr were tested, by using Instron universal testing machine, charpy impact tester, shore D tester, and profilometer respectively.
Results: The transverse strength increased in both the conventional and modified onewhen compared with that cured in air. The addition of 0.5wt% lignin gave the higher effect (78.0017MPa) with highly significant difference found between groups at 40°C polymerizing temperature. While the impact strength in both temperatures in the modified resin revealed increased results than conventional one, 1.25wt% of kraft lignin gave the highest value (12.7355KJ/m2) with highly significant differences found between groups at 80°C polymerizing temperature. Hardness and surface roughness showed also highly significant differences found between groups at 40°C polymerizing temperature, all the groups had increased Hr. than the control one (78.95), while the Ra. decreased for 1.0% ,1.25,1.50 and 1.75 wt% lignin content to (0.26,0.10,0.063, 0.12µm) respectively in 40°C polymerizing temperature, the lowest value present in 1.75 wt% lignin (0.05 µm) at 80°Cpolymerizing temperature.
Conclusions: It seems that increasing the polymerizing temperature to 40°C had a positive effect on the mechanical properties of autopolymerizing acrylic resin and the one enforced by kraft lignin biopolymer in low percentages. Increasing the polymerizing temperature to 80°C will doesn’t have much positive effect but it doesn’t deteriorate the mechanical properties. However, when submitted to increasing the temperature to 80°C, specimens showed a significant increase in impact strength.
Downloads
Article Details
Issue
Section
Licenses and Copyright
The following policy applies in The Journal of Baghdad College of Dentistry (JBCD):
# JBCD applies the Creative Commons Attribution (CC BY) license to articles and other works we publish. If you submit your paper for publication by JBCD, you agree to have the CC BY license applied to your work. Under this Open Access license, you as the author agree that anyone can reuse your article in whole or part for any purpose, for free, even for commercial purposes. Anyone may copy, distribute, or reuse the content as long as the author and original source are properly cited. This facilitates freedom in re-use and also ensures that JBCD content can be mined without barriers for the needs of research.
# If your manuscript contains content such as photos, images, figures, tables, audio files, videos, etc., that you or your co-authors do not own, we will require you to provide us with proof that the owner of that content (a) has given you written permission to use it, and (b) has approved of the CC BY license being applied to their content. We provide a form you can use to ask for and obtain permission from the owner. If you do not have owner permission, we will ask you to remove that content and/or replace it with other content that you own or have such permission to use.Don't assume that you can use any content you find on the Internet, or that the content is fair game just because it isn't clear who the owner is or what license applies.
# Many authors assume that if they previously published a paper through another publisher, they own the rights to that content and they can freely use that content in their paper, but that’s not necessarily the case, it depends on the license that covers the other paper. Some publishers allow free and unrestricted re-use of article content they own, such as under the CC BY license. Other publishers use licenses that allow re-use only if the same license is applied by the person or publisher re-using the content. If the paper was published under a CC BY license or another license that allows free and unrestricted use, you may use the content in your JBCD paper provided that you give proper attribution, as explained above.If the content was published under a more restrictive license, you must ascertain what rights you have under that license. At a minimum, review the license to make sure you can use the content. Contact that JBCD if you have any questions about the license. If the license does not permit you to use the content in a paper that will be covered by an unrestricted license, you must obtain written permission from the publisher to use the content in your JBCD paper. Please do not include any content in your JBCD paper which you do not have rights to use, and always give proper attribution.
# If any relevant accompanying data is submitted to repositories with stated licensing policies, the policies should not be more restrictive than CC BY.
# JBCD reserves the right to remove any photos, captures, images, figures, tables, illustrations, audio and video files, and the like, from any paper, whether before or after publication, if we have reason to believe that the content was included in your paper without permission from the owner of the content.